Low Alloy Steel

6 cases · 26 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: At the Surface clear all

Low Alloy Steel — sub-branches

CMn Steel 13CrMo Steel 4High Strength Low Alloy 7Low Alloy Low Carbon QT 2Low Alloy Medium Carbon QT 23Low Alloy Wear Resistant 1Low Alloy for Thermochemical Treatment 2Microalloyed Steel 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the tooth gear, in a transverse section, close to surface. The material presents light ghost marks that reveal chemical segregations.
80
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Nital Etched Micrography by OMDf - At the Surface
Detail of the opposite side of the plate. No evidence of damage, only small adhesion of the red painting (bottom right part of the figure).
32
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Aspect Before AnalysisDf - At the Surface
The head of the bolts presented the marks that indicated they were manufactured to meet ASTM A449 type 1 bolt, that is a medium strength low alloy steel, quenched and tempered.
148
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Micrographic detail a longitudinal section of the pin, at the surface, showing the case hardened. The pin carburized, quenched and tempered structure presents a gradient of carbon content and consequently a gradient of martensitic structure and hardness. Close to the surface the hardness level is 742 HV1 .
87
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - At the Surface
Aspect of the washout in the 5" drill pipe, in the pipe body, before cleaning the surface.
684
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the cutting surface, slightly irregular. The structural plate is 1 1/4" thick.
48
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Aspect Before AnalysisDf - At the Surface

More from these cases

ML00181 — Wear of a Carburized Hypoid GearM - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Aspect of the fractured tooth in a region presenting pitting, opening voids, and cracks.
52
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface Aspect by SEMDf - At the Surface
ML00142 — Impact of a .308 Winchester on AR500 PlateM - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Microscopically aspect of the plate surface in the center of the bullet impact. The light and smooth surface is the melted bullet on the plate and the dark surface is the steel plate with oxides and very small surface cracks (10 microns length).
30
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - At the Surface
Detailed aspect of the plate surface where there was the bullet impact, by scanning electron microscopy, showing that the bullet has melted and solidified on the surface. The EDS analysis showed Pb-Sb peaks.
32
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - At the Surface
Aspect of the plate surface a little far from the region of bullet impact, by scanning electron microscopy, showing bullet melted islands on the surface. The EDS analysis showed Pb-Sb peaks.
25
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - At the Surface
Detailed aspect of the plate surface a little far from the region of bullet impact, by scanning electron microscopy, showing bullet melted islands on the surface. The EDS analysis showed Pb-Sb peaks.
24
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - At the Surface
Micrography of the plate section, as polished, close to the surface that suffered the impact. No evidences of damage.
26
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface

+8 more from this case →

ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section.
134
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section. The bolt was quenched and tempered to 30HRc and presented a martensitic structure.
124
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic aspect of the rolled thread that was heat treated later. Longitudinal section.
115
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface
ML00081 — Hydrogen Cracking of a Chromium Plated Carburized PinM - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Scanning electron fractography showing that the fracture micromechanism is intergranular close to the surface of the pin, suggesting a hydrogen embrittlement effect at the carburized layer. The cracks were created during the electrolytic plating, and propagated later during service.
45
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - At the Surface
ML00068 — Corrosion Fatigue of a 5" Drill PipeM - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Aspect of the washout in the 5" drill pipe, in the pipe body, after cleaning the surface. The surface presents several parallel tool marks that are not typical in the pipe since the torque is applied in the tool joint.
195
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface AspectDf - At the Surface
ML00033 — Plasma Cut of 1 1/4" Steel PlateM - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Aspect of the 1 1/4" thickness plate cutting surface.
30
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Aspect Before AnalysisDf - At the Surface