High Alloy Steel

3 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Sound Detail focus: Fusion Line clear all

High Alloy Steel — sub-branches

Austenitic Stainless Steel 3Ferritic Stainless Steel 2Martensitic Stainless Steel 1Nickel Alloy Steel 1Super Duplex Stainless Steel 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the tubing fusion line. The welding was conducted in two passes. The average hardness at the heat affected zone of the tubing is 257 HV5.
825
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line Left Side
Micrography of the fusion line close to the cap pass (CP). The weld metal (non etched) is in the left side.
43
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Fusion line micrographic detail. The weld metal is in the right and HAZ in the left.
27
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by SEMDf - Fusion Line

More from these cases

ML00100 — Superduplex Tubing to Forging Welded JointM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Micrography of the forging fusion line. The welding was conducted in two passes. The average hardness of the heat affected zone is 273 HV5.
39
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line Right Side
ML00066 — GMAW Welded Joint in 9%Ni Alloy SteelM - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Micrographic detail of the fusion line in the center of the thickness, where the heat affected zone was reheated by the subsequent passes.
34
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line showing a non reheat heat affected zone of the cap pass. Weld metal (non etched) in the left.
22
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the fusion line etched with Chromic Acid. The weld metal (etched, dendritic) is in the left. There is a white layer that corresponds to planar solidification growth of the melted weld.
26
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Eletrolytically Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line. The white layer is a region of planar growth. Chromic acid, electrolytic etched.
25
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Eletrolytically Etched Micrography by OMDf - Fusion Line
ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Micrography of the weld metal close to the fusion line showing the previous austenite columnar grain boundaries.
25
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Fusion Line