Austenitic Stainless Steel

4 cases · 45 images for “stress corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Aspect of the stub end, that is used in combination with a lap joint flange. In this case it was prepared from a seam welded pipe, longitudinal, also with circunferential weld to the stub face (which means it was not flared). The cracking is circunferential in the non painted region, not associated to any welded area.
435
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View
Optical micrography of a longitudinal section of the fractured bolt, at the thread. The material is austenitic, free from carbides, and the threads were almost removed by the stress corrosion cracks.
756
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Stress Corrosion Cracks
Aspect of the heat exchanger plate showing the rupture of the plate in multiple cracks, starting at the side of the crude oil with high salinity.
727
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Cracking
Regions of the pin thread presenting pitting corrosion.
635
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Localized Corrosion

More from these cases

ML00168 — SCC of Austenitic SS Flange Stub EndM - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Detail of the external side of the stub end showing that the cracking is circunferential, located in a corroded surface, that corresponds to the confined region under the flange.
85
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Cracking
The stub end was manufactured from a plate and the microstructure in a longitudial section shows a refined granular austenitic structure.
62
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrography of a longitudinal section of the stub end showing a refined austenitic structure.
57
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrographic detail of the austenitic structure. Free from grain boundaries carbide precipitation.
53
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Macrographic detail of the longitudinal section of the stub end, showing the external side to the top and the internal side to the bottom. There are multiple cracks starting from the external side.
54
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Longitudinal Section AspectDf - Multiple cracks

+10 more from this case →

ML00157 — Bolts Under Chloride SCC ConditionsM - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Aspect of a 5/16" bolt manufactured in an AISI 316 austenitic stainless steel, that was also operating inside the pressure vessel, but was not yet damaged. It is a hexagonal head bolt, 1 1/2" long, fastened with a hexagonal nut and a lock washer.
118
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View
Low magnification micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides.
100
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides, strain hardened. The hardness values of the material are from 200HV1 to 300HV1, that meets the class 2 of strenght (ASTM A193 B8M class 2).
79
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Detail of the strain hardened austenitic microstructure. Micrography by optical microscope, of the longitudinal section of a bolt, in the center of the thickness.
76
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Strain Hardened
Aspect of a broken 5/16" bolt that was operating inside the pressure vessel in a condition that exceeds the limits of use of the AISI 316 steel. The fracture is located close to the position where there was the bolt head and the threads were "removed" close to the fracture surface.
75
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Fracture

+8 more from this case →

ML00051 — Chloride SCC of 316 Heat Exchanger PlateM - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Macrography of the surface of the cracked heat exchanger plate, manufactured in austenitic stainless steel.
159
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Cracking
Micrography of the plate material presenting a granular austenitic structure, free from precipitation.
122
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Eletrolytically Etched Micrography by OMDf - Austenite
Micrographic detail of the austenitic microstructure of the heat exchanger plate, free from carbides that suggest the adoption of a material in a solution annealed condition, although the high hardness level indicates cold working.
109
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Eletrolytically Etched Micrography by OMDf - Austenite
Micrography presenting the transgranular morphology of the stress corrosion cracks of the austenitic plate. EDS analysis at the plate surface indicated high Cl peaks.
111
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Eletrolytically Etched Micrography by OMDf - Corrosion Cracking
Micrographic detail of a branch transgranular crack typical of CSCC. Moreover, there is no evidence of intergranular precipitation.
99
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Corrosion Cracking
ML00016 — SCC in Free Cutting 303SSM - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Regions of the localized corrosion spots associated to non metallic inclusions.
123
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Non Metallic Inclusions
The macrography of the longitudinal section of the pin (9.5 mm nominal diameter) shows the localized corrosion associated to the non metallic inclusions.
107
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Localized Corrosion
The low magnification micrography of the longitudinal section of the pin shows the localized corrosion associated to the non metallic inclusions.
89
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
The pin microstructure in the longitudinal section shows austenitic structure, free from carbides, and sulfide inclusions that characterize the free cutting condition of this stainless steel.
77
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Non Metallic Inclusions
The micrographic detail of the longitudinal section of the pin shows the localized corrosion associated to the non metallic inclusions.
67
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion

+3 more from this case →