Carbon Steel

2 cases · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: G10200 Detail focus: Sampling and Analysis clear all

Carbon Steel — sub-branches

Low Carbon Steel 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect before cleaning of the heavy U bolt pipe clamp, 38 mm diameter wire, at the fractured position. It is possible to see that it broke in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
522
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Macrography of a longitudinal section of the eye bolt, presenting the fracture in the top of the figure and the threads in the left side of the figure. Details of the fracture of the first thread fillet below the fracture are presented in the next figures.
225
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - NItal Etched MacroDf - Longitudinal Section

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Aspect of the U bolt clamp with partial detachment of the coating (white brown) in a region where the polimeric insert (dirty white) is still in the wire groove at the internal clamp diameter (ID).
91
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Metallographic image of a longitudinal section of the clamp (axis in the vertical direction), showing a refined ferritic perlitic structure.
34
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The clamp presented several cracks, parallel, transverse to the axis. The appearance of the cracks in the metallographic section shows that some cracks propagate and growth with a irregular path.
24
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00120 — Ductile Rupture of a Carbon Steel Eye BoltM - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Apect of the 1/2" ND bumper eye bolt that was fractured (in the left side of the figure) in the position where the nut was tight.
192
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Aspect Before AnalysisDf - General View