Copper Alloy

5 cases · 13 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Scanning Electron Microscope clear all

Copper Alloy — sub-branches

Aluminum Brass 1Aluminum Bronze 2Brass 3Cupronickel 1Pure Copper 1Tin Bronze 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Scanning electron microscopy of the internal surface of the tube, showing that under the deposits there are regions of localized corrosion.
30
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Internal Surface
The through wall cracking was opened and the fracture surface presents a full integranular morphology, typical of an intergranular stress corrosion cracking.
79
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Fractography by SEMDf - Stress Corrosion Cracks
Aspect of the coaster surface grooves, by scanning electron microscopy in a low magnification, showing in the right side the flat region that serves as a support; and in the left side the decorative grooves. The smooth surface in the groove suggests that the coasters were manufactured by casting.
66
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Aspect of the surface of the platesheet at a corroded area, showing the selective attack effect.
99
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Corrosion
The fracture micromechanism is ductile for the pin that has been sheared in a condition of controlling the load carrying. Elongated Dimples.
453
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Fractography by SEMDf - Elongated Dimples

More from these cases

ML00170 — MIC in Aluminum Brass TubesM - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Microscopic detail, by scanning electron microscope, of a region where there is a localized dissolution at the internal surface of the tube. The deposits are adhered at the surface and under the deposits, the analysis indicated increased sulfur levels, suggesting SRB (sulfate reduced bacteria) effects.
31
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Pitting
Scanning electron microscopy aspect of the region inside of a pit. The aspect is of a chemical attack, generated by the metabolic by-products of the adhered microorganism. The effect is of a localized dissolution and the granular tube microsctruture is revealed.
40
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Corrosion
ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Fractographic detail of the through wall cracking after opening, presenting a full integranular morphology, typical of an intergranular stress corrosion cracking.
79
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Fractography by SEMDf - Stress Corrosion Cracks
ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Detail of the previous photo showing the flat surface in the right side and the grooves in the left side. The flat side is scratched and the grooves presented a smooth finishing (with dendritic morphology).
57
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Detail of the flat scratched region of the coaster surface. The dark grey "nodules" are lead (Pb) base inclusions.
50
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Detail of the groove region, showing a typical casting morphology at the surface: smooth and presenting a dendritic aspect with interdendritic shrinkage. Some dark grey "nodules" with Pb inclusions are also observed.
51
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
There are some regions in the coaster surface where pores associated to shrinkage is evident.
49
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - Casting defects
ML00007 — Free Machining Brass in Shear PinM - BrassP - Machined PartAp - LiftingCd - Shear
The fracture surface is ductile and the micromechanism is dimples, elongated due to the shearing action.
83
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Fractography by SEMDf - Ductile Fracture