Weld Metal

3 cases · 14 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 182 clear all

Weld Metal — sub-branches

Weld Metal 8Weld Metal in the Cap 2Weld Metal in the Center 3Weld Metal in the Root 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The columnar grains of the weld metal in the cap presented a martensitic structure.
60
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal of the pipe to the fitting. It is possible to see columnar grains and recristalized grains. In the same way, the yellow/white is the austenite and the blue/red is the ferite.
67
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Micrographic detail of the tempered martesite weld metal close to the fusion line. The columnar grains can be observed .
23
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Weld Metal

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Micrography of the weld metal of the pipe to the fitting.
63
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Micrographic detail of the weld metal of the pipe to the fitting. Yellow/white austenite and red/blue ferrite (delta).
59
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Cap pass in the weld metal, presenting a large amount of delta ferrite (retained) due to a probable quick cool of the pool during welding (since this pass is too thin, perhaps a remelting). Although it is not good to present this microstructure, it did not affect the failure.
54
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Micrographic detail of the weld metal tempered martensitic microstructure.
25
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Micrography of the weld metal in the center of the weld, showing a martensitic microstructure.
17
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Weld Metal in the Center
Weld metal micrographic detail showing a tempered martensitic microstructure.
14
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Weld Metal
Micrographic detail of the root pass, welded with GTAW, presenting a tempered martensitic microstructure.
12
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Weld Metal in the Root
Micrography of a reheated fill pass.
10
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Weld Metal in the Center

+3 more from this case →