Sampling and Analysis

3 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: G41400 clear all

Sampling and Analysis — sub-branches

General View 3Longitudinal Section 4

Results

SortNewestOldestTitle A-ZTitle Z-A
The shaft was removed from service without a failure. It was 4' long and the diameters varied from 2 1/2" to 4 1/2". It was analyzed to be specified for purchasing a new one but properties evidenced bad ductility and brittle behavior even at ambient temperature, associated to a microestruture "as hot rolled".
1238
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken stud that was fastening a flanged line in a subsea body (tapped hole) using a nut. The fracture, transverse to the stud axis, occurred exactly at the body to flange interface. Adjacent to the fracture, all thread fillets (positioned inside the flange hole) presented cracks at the bottom of the thread. The stud was operating during seven years and was not corroded, indicating it was protected by the anodes. There are also deposits in the fillets suggesting the cathodic protection was effective even inside the flange hole.
799
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Allen stud, 1/2" nominal diameter, cadmium plated and chromate treated, cracked during assembling external parts in a gate valve.
63
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00152 — Low Alloy Steel Pump ShaftM - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
The longitudinal section of the shaft shows a coarse structure. Only very close to the surface the structure is slightly refined.
99
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - NItal Etched MacroDf - Longitudinal Section
The longitudinal section of the shaft, in the center of the thickness, shows a coarse structure, and a ferritic/bainitic structure with pearlite islands.
97
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The longitudinal section of the shaft, at the surface, also shows a coarse structure, and a ferritic/bainitic structure with pearlite islands. There is only a small refining in the previous austenite grain boundaries, indicating that the material was not heat treated.
75
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00127 — Hydrogen Cracks of Cadmium Plated StudsM - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Macrography of a longitudinal section of the stud, showing the flat fracture of brittle aspect.
46
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Longitudinal Section