Sampling and Analysis

3 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Seamless tube Microstructure: Bainite Capture method: Optical Microscope clear all

Sampling and Analysis — sub-branches

Base Metal 2Close to the External Surface 2Close to the Internal Surface 2External Surface 1Fusion Line 2Weld Metal 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the external tube surface, presenting a crack at the weld margin. This cracking could have been created by thermal induced cycles (fatigue), but it did not propagate into the tube wall. In some regions of the external side of the tube the weld metal was detached.
77
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - External Surface
Micrography of the longitudinal section of the tube, close to the external surface, presenting a thick deposit.
110
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Close to the External Surface
Low carbon plate base metal presenting the ferritic perlitic structure.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

More from these cases

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Micrography of the external tube surface, presenting the cracking at the margin of the weld. This cracking could have been created by thermal induced cycles (fatigue), but it did not propagate into the tube wall.
85
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Fusion Line
ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrography of the longitudinal section of the tube, close to the internal surface, presenting a thick deposit.
98
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography of the longitudinal section of the tube, close to the external surface. A scale is evident at the surface as well as a carburizing layer.
83
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of the longitudinal section of the tube, close to the internal surface. A thick scale is evident, but no microstructural changes compared to the center of the tube.
92
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
High Strenght Low Alloy steel tube, base metal, presenting the bainitic structure.
54
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the low carbon steel plate at the fusion line, presenting a bainitic structure at the HAZ and ferritic structure in the weld metal.
82
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the weld metal in the center of the fillet showing a 100% acicular ferrite that is a microestructure of a high strenght steel, evidenced the effect of the dilution of the tube chemistry in the weld metal.
40
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal