Sampling and Analysis

2 cases · 21 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Non qualified Capture method: Optical Microscope clear all

Sampling and Analysis — sub-branches

Base Metal 5Heat Affected Zone 10Weld Metal 6

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite structure in the columnar (previous austenitic) grains has suffered degradation due to the long heat treatment cycle (12 hours) in high temperature.
97
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Low magnification micrography of the plate base metal, presenting granular structure not clearly identified and aligned particles.
88
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal

More from these cases

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite has suffered degradation due to the long heat treatment cycle (12 hours) in a temperature of 640°C, that is higher than the recommended for the D2 filler metal.
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the base metal, in low magnification, showing regions of segregations in a quenched and tempered martensitic structure.
52
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the base metal showing a quenched and tempered martensitic structure. The base metal adopted in the test coupon presented a hardness level of 217HB (Brinell hardness of the certificate) and after the PWHT cycle the measured base metal hardness is 224 HV10.
59
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the heat affected zone at the face of the joint. It is possible to see that even close to the fusion line the material was reheated in high temperature, suggesting that the temper bead was effective.
53
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the heat affected zone at the face of the joint, close to the fusion line. The hardness level at the HAZ was 248 HV10.
58
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

+6 more from this case →

ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Micrography of the plate base metal, presenting granular structure evidenced by the different shadows in the grains.
76
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal
Micrographic detail of the aligned particles in the plate base metal. The grain boundaries are not clearly identified in this higher magnification.
73
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal
Low magnification micrography of the welded joint at the heat affected zone of the flat position, in the last bead (face). Longitudinal section of the plate, transverse to the welded joint.
68
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Last Bead HAZ
Micrography of the welded joint at the heat affected zone of the flat position, in the last bead (face). Longitudinal section of the plate, transverse to the welded joint.
64
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Last Bead HAZ
Micrographic detail of the welded joint at the heat affected zone of the flat position, in the last bead (face). Longitudinal section of the plate, transverse to the welded joint.
57
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Last Bead HAZ

+3 more from this case →