Sampling and Analysis

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: S17400 Capture method: Naked Eye or Stereoscope clear all

Sampling and Analysis — sub-branches

General View 1Longitudinal Section 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the longidutinal section of a non broken allen bolt, at the threaded body to bolt head transition. The granular structure is different through the bolt, with refined structure in the threaded body and coarse at the transition.
44
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Longitudinal Section
Fracture view presenting two diferente aspects, brittle in the bottom of the figure and in the center (most part of the fracture) and ductile in the top of the figure. Nominal diameter of the bolt 1 1/2".
203
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - General View

More from these cases

ML00074 — Hydrogen Cracking of a 17-4 PH Subsea BoltM - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Macrography of a longitudinal section of the broken bolt, at the fracture position, showing that the fracture is partially flat (left side), where the macroscopically aspect is brittle, and a final ductile fracture (right side). Interesting to note that there is a large longitudinal crack, secondary (transverse to the fracture surface).
143
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Longitudinal Section