Sampling and Analysis

12 cases · 14 images for “embrittlement”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Aspect Before Analysis clear all

Sampling and Analysis — sub-branches

General View 14

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Aspect of the broken stud that was fastening a flanged line in a subsea body (tapped hole) using a nut. The fracture, transverse to the stud axis, occurred exactly at the body to flange interface. Adjacent to the fracture, all thread fillets (positioned inside the flange hole) presented cracks at the bottom of the thread. The stud was operating during seven years and was not corroded, indicating it was protected by the anodes. There are also deposits in the fillets suggesting the cathodic protection was effective even inside the flange hole.
799
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Allen stud, 1/2" nominal diameter, cadmium plated and chromate treated, cracked during assembling external parts in a gate valve.
63
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken bolt, 5/8" Allen, socket head cap screw, originally 1 3/4" long, broken in subsea service under cathodic protection. The bolt presents a zinc coating.
116
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the fracture that occurred in the connection between the pin of one DP and the box of other DP, in the pin side. The photo presents the pin still connected in the box. The flat fracture indicates a brittle behavior.
641
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of three pins that were operating in a hydraulic system. Adjacent to the fracture of the broken pin (the one that is in the right side of the figure) it is possible to see multiple surface craks and detachment of the surface chromium layer.
88
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Fracture appearance of the 1 1/4" diameter link. The fracture is flat and presented no evidences of plastic deformation, suggesting a brittle behavior.
54
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Brittle aspect of the failure of the conector in the male thread. Both sides of the fracture.
96
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the bolt fracture. The fracture appearance is irregular and there are several secondary cracks from thread fillets.
245
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Aspect of the fracture of a small Allen bolt, nominal diameter 5/8" 1 3/4" long, class 12.9, that was operating in subsea environment during 5 years. The fracture is rusted but the thread still presents the zinc coating.
81
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View