Welded Joint

6 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Bainite clear all

Welded Joint — sub-branches

Welded Joint 3

Results

SortNewestOldestTitle A-ZTitle Z-A
The 6 1/2" nominal diameter longitudinal seam welded pipe is internally cladded with Alloy 625. The pipe was manufactured by forming a cladded plate (probably welded by rolling) and welding it longitudinally. The pipe was heat treated (quenched and tempered) after the seam weld.
96
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
The 4 1/2" nominal diameter seamless pipe internally overlaid with Alloy 625. This pipe corresponds to a 90° curve. The overlaid pipe was heat treated before and after bending. The final quenching and tempering heat treatment was conducted to meet API 5L X70 properties.
113
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
Macrography of the tubular forging, butt welded using a LAS filler metal, and overlaid using Inconel 625 filler metal. The micrographic characterization was conducted for the HAZ of the overlay and for the HAZ of the butt weld, at the root position (with several welding cycles) and at the face.
608
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Electrolytically Etched MacroDf - Welded Joint
Macrography of the fillet welded joint between the 3" ND tube and the 3/4" thick plate. See the schematic drawing in the next figure
56
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the typical welded joint between the superior plate (8mm) and the inferior plate (12 mm) using one SAW fillet. The superior plate is welded in the thickness and the inferior plate is welded at the surface in this overlap joint. See the schematic drawing in the next figure
95
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Hot cracking at the fusion line of the connector side, in a welded joint between a forging and a pipe, in a macrographic sample. The region of the heat affected zone of the connector presents a dendritic aspect suggesting that the forging reduction rate of the connector was not too high and did not broke the cast structure.
110
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint

More from these cases

ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Schematic drawing presenting the position of the cracking, at the margin of the weld in the tube and underbead.
47
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Identification drawingDf - Welded Joint
ML00069 — Liquation Cracks in SAW of Low Carbon SteelM - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Schematic drawing presenting the different zones at the welded joint.
88
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Identification drawingDf - Welded Joint