Welded Joint

2 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Non qualified clear all

Welded Joint — sub-branches

Flat Position 3Horizontal Position 3Overhead Position 3Vertical Up Position 3Welded Joint 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the welded joint taken from the vertical up part of the joint, presenting the root in one pass, the fill of the joint in three passes, the cap in three passes and two temper bead passes. The 10" diameter tube, 9.5mm thick, was welded by GTAW in the root (80SD2 filler metal) and by SMAW for fill, cap and temper bead passes (10018-D2 filler metal).
77
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - NItal Etched MacroDf - Welded Joint
Summary of the welding conditions and qualification test results. NON QUALIFIED WPS. The individual parameters for each welding position are presented in the legend of each macrography, that also presents the amount of beads.
117
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - WPS summaryDf - Welded Joint

More from these cases

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
WPS welded in 6G qualification welding position and tested according to ASME IX and NACE ISO 15156. Minimum preheating of 250°C. Two temper bead passes. PWHT at 640°C during 12 hours. Tube diameter 10". Thickness 3/8". V groove 70°. Root opening 1/8". NOT APPROVED due to ULTIMATE STRENGHT lower than the base metal minimum requirements.
87
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - WPS summaryDf - Welded Joint
ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Macrography of the flat position welded joint. It was welded in three passes, with the following parameters. Root pass - 157A, 21V, 146mm/s (wire speed), 3.2 mm/s (welding speed), 1090 J/mm. Second pass - 161A, 21V, 146mm/s (wire speed), 4.2 mm/s (welding speed), 833 J/mm. Third pass - 155A, 21V, 146mm/s (wire speed), 5.1 mm/s (welding speed), 664 J/mm.
48
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Flat Position
Macrographic detail of the flat position welded joint, showing the three passes. The large extension of the heat affected zone in the root reveals the too high imposed energy, melting out of the root gap. The shining spots are pores.
42
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Flat Position
Macrography of the horizontal position joint. It was welded in three passes, and one additional pass from the root. Root pass - 153A, 20V, 156mm/s (wire speed), 3.5 mm/s (welding speed), 933 J/mm. Second pass - 162A, 20V, 156mm/s (wire speed), 5.8 mm/s (welding speed), 592 J/mm. Third pass - 155A, 19V, 156mm/s (wire speed), 5.9 mm/s (welding speed), 523 J/mm. Additional at the root - 161A, 23V, 187mm/s (wire speed), 8.5mm/s (welding speed), 467J/mm.
47
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Horizontal Position
Macrographic detail of the horizontal position welded joint, showing the three passes welded from one side and the fourth pass welded after removing the ceramic backing. Big pores and liquation were identified.
40
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Horizontal Position
Macrography of the vertical up position welded joint. It was welded in three passes, with the following parameters. Root pass - 115A, 21V, 162mm/s (wire speed), 2.6 mm/s (welding speed), 1090 J/mm. Second pass - 143A, 21V, 162mm/s (wire speed), 5.5 mm/s (welding speed), 594 J/mm. Third pass - 144A, 21V, 162mm/s (wire speed), 6.1 mm/s (welding speed), 979 J/mm.
39
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Vertical Up Position

+7 more from this case →