Welded Joint

5 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The 6 1/2" nominal diameter longitudinal seam welded pipe is internally cladded with Alloy 625. The pipe was manufactured by forming a cladded plate (probably welded by rolling) and welding it longitudinally. The pipe was heat treated (quenched and tempered) after the seam weld.
96
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
The 4 1/2" nominal diameter seamless pipe internally overlaid with Alloy 625. This pipe corresponds to a 90° curve. The overlaid pipe was heat treated before and after bending. The final quenching and tempering heat treatment was conducted to meet API 5L X70 properties.
113
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
Macrography of the welded joint taken from the vertical up part of the joint, presenting the root in one pass, the fill of the joint in three passes, the cap in three passes and two temper bead passes. The 10" diameter tube, 9.5mm thick, was welded by GTAW in the root (80SD2 filler metal) and by SMAW for fill, cap and temper bead passes (10018-D2 filler metal).
77
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - NItal Etched MacroDf - Welded Joint
Microstructure of the welded region of the padeye, at the fusion line. The weld metal is dendritic, austeno ferritic, in the left side of the figure. The heat affected zone is in the center of the figure and shows no changes in relation to the base metal. The padeye base metal is to the right side of the figure.
120
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Welded Joint
Macrography of the tubular forging, butt welded using a LAS filler metal, and overlaid using Inconel 625 filler metal. The micrographic characterization was conducted for the HAZ of the overlay and for the HAZ of the butt weld, at the root position (with several welding cycles) and at the face.
608
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Electrolytically Etched MacroDf - Welded Joint

More from these cases

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
WPS welded in 6G qualification welding position and tested according to ASME IX and NACE ISO 15156. Minimum preheating of 250°C. Two temper bead passes. PWHT at 640°C during 12 hours. Tube diameter 10". Thickness 3/8". V groove 70°. Root opening 1/8". NOT APPROVED due to ULTIMATE STRENGHT lower than the base metal minimum requirements.
87
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - WPS summaryDf - Welded Joint
ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Micrographic detail of the fusion line of the welded joint of the padeye. The connector where the padeye was installed was welded to the case, but presented no evidences of corrosion.
110
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Welded Joint