Weld Metal

3 cases · 14 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Duplex Ferritic Austenitic clear all

Weld Metal — sub-branches

Weld Metal 5Weld Metal in the Cap 3Weld Metal in the Center 3Weld Metal in the Root 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the weld metal of the pipe to the fitting. It is possible to see columnar grains and recristalized grains. In the same way, the yellow/white is the austenite and the blue/red is the ferite.
67
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Micrography at the center of the weld metal, showing the interface between the two passes. The average hardness of the weld metal is 260 HV5.
49
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Center
Micrography of the root weld metal. Duplex ferritic austenitic structure with Widmanstatten morphology.
30
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Root

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Micrography of the weld metal of the pipe to the fitting.
63
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Micrographic detail of the weld metal of the pipe to the fitting. Yellow/white austenite and red/blue ferrite (delta).
59
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Cap pass in the weld metal, presenting a large amount of delta ferrite (retained) due to a probable quick cool of the pool during welding (since this pass is too thin, perhaps a remelting). Although it is not good to present this microstructure, it did not affect the failure.
54
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
ML00100 — Superduplex Tubing to Forging Welded JointM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Micrography at the center of the weld metal.
41
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Micrography at the center of the weld metal, last pass.
39
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Cap
Micrography at the center of the weld metal, first pass that is reheated.
38
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Root
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Micrographic detail of the root weld metal. Duplex ferritic austenitic structure with Widmanstatten morphology.
30
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Root
Micrography of the center of the weld metal (fill pass). Duplex ferritic austenitic structure.
24
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Center
Micrographic detail of the center of the weld metal (fill pass). Duplex ferritic austenitic structure.
27
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Weld Metal in the Center
Micrography of the weld metal (cap) at the surface. It is clear that the last bead of the weld was remelted in an autogenous condition, probably to create a better finish, since the layer is less than 2 mm deep. This is a typical bad practice since a large amount of ferrite is retained by the quick cooling.
31
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Cap
Micrographic detail of the weld metal (cap) at the surface. A large amount of ferrite is retained by the quick cooling at the surface.
24
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal in the Cap