Weld Metal

2 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Chemical Industry clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography showing the weld metal, full of pores, indicating that the field welding was not properly shileded.
50
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal structure. At the interface between the two passes, close to the AA 3003 pipe.
50
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Weld Metal

More from these cases

ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Micrography of the weld metal at the fillet weld where the cracking started, showing several brittle microcracks that corresponds to the regions where the fractography showed secondary crackis.
35
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal brittle microcracks, in regions with hydrides formation.
32
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Hydrides in Titanium Weld
2
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Micrography by OMDf - Weld Metal
ML00059 — Intergranular Corrosion of Aluminum PipingM - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Weld metal structure.
44
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal structure.
53
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Weld Metal