Transverse Section

4 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Granular clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the fork handle in the transverse section, curved, presenting differences between grain size and morphology. In the middle section there are elongated grains and close to the surfaces there are smaller and more equiaxed grains.
82
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Transverse Section
Aspect of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in a section transverse to the impact position that is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet.
23
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Transverse Section AspectDf - Transverse Section
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
76
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
The nut was sectioned in the longitudinal direction to reveal the position of the Nylon insert.
59
VIEW
ML00062 / Apr.2017
Inconel 718 Lock Nut with Polymer Insert
M - NiCrFe AlloyP - Cold FormedAp - PipingCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - Transverse Section

More from these cases

ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Macrography of the 3/8" thickness aluminum alloy plate, in a section. The side of bullet impact is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet (to the bottom of the figure).
19
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched MacroDf - Transverse Section
Macrographic detail of the 3/8" aluminum alloy plate. The side of bullet impact is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is in the left side of the figure.
19
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched MacroDf - Transverse Section
Macrographic detail of the 3/8" thickness aluminum alloy plate. The side of bullet exit is to the bottom of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is in the right side of the figure
7
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched MacroDf - Transverse Section
ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
64
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section