Heat Affected Zone

1 case · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Cladding clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
66
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

More from these cases

ML00102 — AISI 4130 Forging Welded and OverlaidM - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
61
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ), butt weld face. The structure is tempered martensite because the welded joint was PWHT at 630°C. The original forging was normalized and tempered at 660°C.
48
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) at the face of the butt weld. The structure is a tempered martensite because the joint was PWHT at 630°C. The original forging was normalized and tempered at 660°C.
43
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ), butt weld root. The structure is ferritic bainitic because of the multiple reheatings in high temperature.
51
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ), butt weld root. The structure is ferritic bainitic because of the multiple reheatings in high temperature.
34
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone