General View

6 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
641
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
300
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
The welded joint of the flat position is shown from the root side. It is possible to see that the use of the backing generated the possibility for melting the base metal out of the groove, without detection of this condition during welding, responsible for creating defects and avoiding the WPS qualification.
102
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Aspect Before AnalysisDf - General View
Draft of the completion riser after removal of the external case showing the hydraulic line position where the 316 tubing is welded by orbital autogenous GTAW to the Nitronic fitting (stab). In the design of these hydraulic lines, the position of the cracking in the fitting is associated to a slightly bent condition of the fitting due to the misaligment of the tubing axis and the stab axis in the connector, visible in the draft.
1081
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Identification drawingDf - General View
Aspect of the fitting welded to a tubing, ND 5/8" in a hydraulic line. The through wall cracking is longitudinal in the fitting side.
1031
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
The connector was welded to the pipe from both (internal and external) sides, a PWHT was applied and the part was machined. The UT indication was detected during final inspection.
78
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Hydrides in Titanium Weld
1
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
The welded joint of the vertical up position is shown from the root side. It is possible to see that the use of the backing generated the possibility for melting the base metal out of the groove, without detection of this condition during welding, responsible for creating defects and avoiding the WPS qualification.
122
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Aspect Before AnalysisDf - General View
ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Aspect of the hydraulic line samples removed from service to be analyzed. Tubing and welded joint (bottom sample) between the 316 tubing (left side of the sample) and the nitronic fitting (right side of the sample). The cracking is located 10 mm far from the weld, autogenous orbital GTAW.
108
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View