Fusion Line

1 case · 1 image

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Boiler clear all

Fusion Line — sub-branches

Fusion Line 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the external tube surface, presenting the cracking at the margin of the weld. This cracking could have been created by thermal induced cycles (fatigue), but it did not propagate into the tube wall.
85
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Fusion Line