Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Image of the external surface of the valve body at the region where the Alloy 625 insert was fillet weld to the SDSS valve body. The surface was later machined, so it is possible to see only a mark indicating where the weld is. The brittle crack is arrested at the margin of the weld. It is possible to see strong deformation at the crack tip when it arrives the weld.
41
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the external surface of the tube, presenting the aspect of the cap and temper bead passes, after welding and heat treatment.
54
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Aspect Before AnalysisDf - External Surface
Scanning electron microscopy image of the external surface of the line at the cracking position showing multiple cracks, branched, transverse to the line axis.
79
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Detail of the longitudinal through wall cracking in the fitting welded to a tubing, ND 5/8" in a hydraulic line.
87
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - External Surface

More from these cases

ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
The aspect of the fitting surface by SEM shows multiple cracks. Interesting to observe a stained region (dark grey) that corresponds to regions where the material passivation was destroyed.
43
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Detail of one region that had the passivation layer destroyed .
45
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Aspect by scanning electron microscopy of the cracking at the external surface of the fitting.
47
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Aspect by scanning electron microscopy of the cracking at the external surface of the fitting. Interesting to observe that the cracks are deformed.
39
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface