Close to the External Surface

3 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Engine clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Fracture surface of the tubing, close to the outer diameter.
47
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Close to the External Surface
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the external surface (left side). It is possible to see smaller graphite flakes, interdendritic .
79
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the External Surface
The micrography of the transverse section shows coarse grains and biphasic structure. Alpha grains and a lamellar eutectoid structure can be observed in the material.
464
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface

More from these cases

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
The fracture surface of the casting cylinder presented, close to the external surface, a more ductile aspect of the fracture.
58
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Close to the External Surface
Micrography of the longitudinal section of the cylinder, at the external diameter (right side of the figure), presenting smaller interdendritic graphite flakes in a ferritic-perlitic matrix.
37
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of the painted external surface of the cast cylinder.
25
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polishedDf - Close to the External Surface
Micrographic detail of the painted external surface of the cast cylinder.
26
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the External Surface
Micrographic aspect of the cast cylinder section at the fracture position (top of the figure), close to the external surface (left side). It is possible to see a change in the graphite morphology and matrix.
27
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the External Surface

+2 more from this case →

ML00044 — Centrifugally Cast CuAl BushingM - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Micrographic detail of the structure at the external surface.
58
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface