Zn Layer

1 case · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Mechanical Industry clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the casting at the surface, presenting a zinc layer deposited in a hot dip process. The thickness of the layer is about 0.3mm in this position, that is higher than expected for this process. The steel substrate is not revealed because the etch was light and the zinc layer protects the low aloy steel during the etch.
93
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by SEMDf - Zn Layer

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrographic detail of the zinc layer at the surface.
88
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Zn Layer
Scanning electron fractography (originally 500x), showing zinc deposits at the fracture surface.
72
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Zn Layer
Micrographic detail of the section transverse to the fracture (top of the figure), suggesting the intergranular morphology (at the previous austenite grain boundaries) and the deposits of zinc over the fracture that create a condition of protection of the base metal during the metallographic etch, and the material is not fully etched.
58
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Zn Layer
Micrographic detail of the zinc at the fracture surface.
57
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Micrography by OMDf - Zn Layer
Micrographic detail of the branch cracking parallel to the fracture, as polished, showing that the cracks are filled with zinc.
47
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - As polished micrographyDf - Zn Layer

+1 more from this case →