Martensite

4 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 4130 clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body. Uniform structure.
44
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the longitudinal section of the bolt in the center of the thickness (ND 5/8") showing a uniform martensitic structure.
67
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the pin close to the interface with the spray and fuse layer. Transverse section. The fuse is conducted in high temperature and the pin was quenched and tempered after the thermal spray deposition and fuse by flame (in this case the melting of the applied layer was conducted by a oxifuel flame.
21
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensitic structure of the tubular 4130 forging butt weld HAZ (at the face). The martensite was formed during welding, not reheated (because it was the last bead in that position), and tempered during PWHT.
42
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Martensite

More from these cases

ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of sheared pipe, showing strong plastic deformation at the fracture. The structure shows the shear effect at the fracture.
15
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the martensitic structure, uniform in the longitudinal section of the bolt, in the center of the thickness (ND 5/8"). The hardness values of the bolts varied from 39 to 41 HRc.
63
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
ML00109 — Thermal Spray and Fuse Layer in Forged PinM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Micrographic detail of the tempered martensite structure close to the interface with the spray and fuse layer. Transverse section. The fuse is conducted in high temperature and the pin was heat treated after the thermal spray deposition and fuse.
16
VIEW
ML00109 / Jan.2018
Thermal Spray and Fuse Layer in Forged Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Thermal spray
Cm - Nital Etched Micrography by OMDf - Martensite