Coating Layer

2 cases · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Surface layer of Thermal Spray clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrographic aspect of the sleeve longitudinal section where the coating was applied in the external side (top of the figure). It is possible to see that the sleeve was manufactured by centrifugal casting, with elongated grains from the external side, and equiaxial grains close to the internal side (bottom of the figure). There is a weaved interface between the sleeve and the first layer of thermal spray coating, 1 mm thick; and a second layer of thermal spray coating, 0.2mm thick (almost imperceptible at this low magnification).
49
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MacroDf - Coating Layer
Micrography of the thermal spray (TS) layer showing the different alloys, gray oxides and black voids. The Ni base TS alloy is of a yellow colour at the interface with the shaft substrate (in the left). The Cr base TS alloy appears white, similar to the shaft substrate. Longitudinal section of the shaft.
42
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer

More from these cases

ML00108 — Thermal Spray Layer in a Pinion ShaftM - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Micrographic detail, as polished in a longitudinal section, of the interface between the shaft substrate and the thermal spray layer. In the left it is the shaft substrate also presenting parts of aligned inclusions (gray). In the center it is the Ni base TS alloy and in the right it is the Cr base TS alloy. There are also black voids and grey oxides.
33
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer
Micrography of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and tempered structure. Longitudinal section.
32
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Micrographic detail of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and tempered structure. Longitudinal section.
33
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Micrographic detail of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and (over) tempered structure. Longitudinal section.
35
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer