Localized Corrosion

6 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
MIC in Aluminum Brass Tubes
2
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Localized Corrosion
Micrography of the pipe in the leakage area, showing the preferential corrosion in the center of the autogenous weld and oxides inside the crevice, that appearas as a cracking but that is only a localized anodic process.
66
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Localized Corrosion
Micrographic detail of the damaged region close to the external surface, presenting a shallow localized dissolution/corrosion.
48
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Localized Corrosion
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition.
85
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
Intergranular corrosion at the fusion line of the AA 6063 pipe.
81
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Localized Corrosion
The low magnification micrography of the longitudinal section of the pin shows the localized corrosion associated to the non metallic inclusions.
89
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion

More from these cases

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Micrographic detail of the autogenous seam weld. The localized dissolution occurrs exactly at the weld metal that presents a bainitic structure of average hardness about 230HV, compared to the heat affected zone presenting average of 202 HV and the base metal presenting average of 180HV.
57
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Localized Corrosion
Micrographic detail presenting the slighltly decarburized ferritic structure, with inclusions, in the center of the weld, surrounded by a bainitic structure and the preferential corrosion in the weld.
51
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Localized Corrosion
ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Micrography of the damaged region close to the internal surface, presenting a deep pitting corrosion morphology.
40
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Localized Corrosion
ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition.
72
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition. Even non metallic inclusions did not accelerate corrosion since the extension of the inclusions was not too long and they were not connecting to others.
76
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition. Even non metallic inclusions did not accelerate corrosion since the extension of the inclusions was not too long and they were not connecting to others.
81
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
ML00059 — Intergranular Corrosion of Aluminum PipingM - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Intergranular corrosion at the fusion line of the AA 6063 pipe, that presents strong precipitation.
89
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Localized Corrosion
Micrographic detail of the intergranular corrosion at the fusion line of the AA 6063 pipe.
72
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Localized Corrosion
ML00016 — SCC in Free Cutting 303SSM - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
The micrographic detail of the longitudinal section of the pin shows the localized corrosion associated to the non metallic inclusions.
67
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion