General View

7 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Brittle Behavior clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Tool fixture 5" long, nominal diameter 2", presenting a recess 1/2" deep from two sides. The rupture occurred about 2" from the end of the rod. Scale in milimeters.
523
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken spring. The wire is 36 mm diameter and the ourter diameter of the spirals is 320 mm. It was broken in different locations.
434
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
General view of the broken socket. The failure occurred during service, when the tool was tightening 3 3/4" bolts at 75% of the torque capacity. The fracture occurred associated to the smaller section of the socket, thickness of 13 mm, at the corner of the radio, that is a stress concentration raiser.
602
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Fractured position of the casting cylinder of 10.5 mm thickness (minimum measured thickness) showing a brittle behavior (lack of plastic deformation), typical of overloading a material with 1% ductility (measured in the tensile test). This is the view of the internal surface of the cylinder, presenting regions of localized thinning in this surface that was in contact with (treated) cooling water. The external side of the cylinder was painted.
918
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - General View
Aspect of the external side of the connector, with a longitudinally crack of a brittle aspect. It is a 5/8" connector (15.8 mm).
133
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken padeye. The outer diameter is about 10" and the thickness of the casting is about 2".
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken shear pin that was manufactured in a martensitic stainless steel forged bar, machined with the external diameter of 50mm, the internal diameter of 20mm and the shearing diameter of 25mm (shearing thickness 2.5mm). The fracture, in the right side of the figure, is not fully flat as should be expected for a shearing mechanism.
54
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00172 — Brittle Fracture of a LAS Valve SpringM - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Rusted aspect of the spring surface.
26
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
General view of the broken socket. It was broken in two parts and shows no evidences of plastic deformation associated to the rupture.
93
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
General view of the broken socket, showing no plastic deformation asociated to the rupture. Looking from this side it is possible to see that the fracture followed the interface of the stem with the socket head.
80
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View