Damage

7 cases · 26 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Bainite Capture method: Optical Microscope clear all

Damage — sub-branches

Corrosion Cracking 2Crack 3Cracking 3Fracture 2Intergranular Cracking 3Microcracks 2Multiple cracks 1Parallel cracks 2Scale 3Segregated Regions 2Transgranular Cracking 3

Results

SortNewestOldestTitle A-ZTitle Z-A
The internal side of the tube presented multiple cracks, filled with oxides, blunt-tipped, typical of a corrosion fatigue cracking mechanism.
160
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - As polished micrographyDf - Parallel cracks
Micrographic detail of the longitudinal section of the tube, close to the external surface, presenting a thick deposit.
102
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Scale
Micrographic detail of an intergranular secondary crack (adjacent to the broken surface) propagating from the hard chromium layer.
75
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrography of the welded joint fusion line presenting the liquation cracking. The weld metal is in the right side (bottom) and the forged connector heat affected zone is in the left side (top).
83
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of the fracture at the superior plate (8 mm thickness). The fracture occurred in the coarse grain heat affected zone.
60
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fracture
The micrography shows the region underbead, of the tube HAZ, responsible for the hydrogen cracking (fracture in the right side of the photo - black). The hardness of the HAZ is about 600 HV.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking
Welded region etched to reveal impurities. The banded structure creates a continuous network parallel to the weld metal.
50
VIEW
ML00013 / Apr.2017
Welding Cracks in Mooring Chain
M - Low Alloy Low Carbon QTP - Welded PartAp - OffshoreCd - Welding Defect
Cm - Micro by OM, picric acid+FeCl3+H2O etchDf - Segregated Regions

More from these cases

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Micrographic detail of the corrosion cracking from internal side of the tube, in several points at the tube surface.
156
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - As polished micrographyDf - Corrosion Cracking
Low magnification micrography of the multiple cracks, parallel, transgranular. No evidences of microstrutural changes (heat evolution or decarburization).
127
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking
Micrography presenting the internal tube surface with several parallel cracks, some still in the beginning (less than 0.1 mm deep).
115
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Parallel cracks
Micrography of the crack tip, initiated from the internal tube surface. The crack is transgranular, filled with oxides and blunt-tipped.
109
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking
Micrographic detail of the blunt-tipped crack, transgranular and filled with oxides.
102
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Crack

+6 more from this case →

ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrographic detail of the longitudinal section of the tube, close to the internal surface, presenting a thick deposit.
94
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Scale
Micrography of the longitudinal section of the tube, close to the internal surface. A thick scale is evident, but no microstructural changes compared to the center of the tube.
78
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Scale
ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
48
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
43
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
ML00069 — Liquation Cracks in SAW of Low Carbon SteelM - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Micrography of the fracture at the fillet weld margin. The fracture occurred in the coarse grain heat affected zone of the superior plate (8 mm thickness).
54
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography of the fractured region, from the superior plate side, showing that the intergranular cracking occurred at the coarse grain heat affected zone. The structure is bainitic and there are segregated regions in the previous austenite grain boundaries.
50
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrography of the fractured region, from the weld metal side, showing that the intergranular cracking occurred at the coarse grain heat affected zone. The structure is bainitic and there are segregated regions in the previous austenite grain boundaries.
127
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
ML00013 — Welding Cracks in Mooring ChainM - Low Alloy Low Carbon QTP - Welded PartAp - OffshoreCd - Welding Defect
Micrography of a longitudinal section of the mooring chain, at the main crack position. The crack follows a network of segregations.
48
VIEW
ML00013 / Apr.2017
Welding Cracks in Mooring Chain
M - Low Alloy Low Carbon QTP - Welded PartAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Segregated Regions