Damage

5 cases · 13 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Ductile Behavior Capture method: Optical Microscope clear all

Damage — sub-branches

Crack 1Ductile Crack 4Ductile Fracture 1Fracture 2Layer Detachment 2Plastic Deformation 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the secondary crack from the fracture surface of the WHEEL 1, following the interdendritic precipitates.
36
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Keller Etched Micrography by OMDf - Fracture
Micrography of the longitudinal section of the pipe, at the thicker part of the fracture, showing several secondary cracks opened to the external side of the pipe. There are no problems in the material structure and the cracks are associated to large plastic deformation.
36
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrography of a longitudinal section, at the damage surface of the pin, where the thermal spray layer was partially detached and broken. The through layer breaking is ductile, typical of an overloading condition caused by the localized bending of the pin.
109
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
Micrography as polished of the longitudinal section of the bolt at the fracture position. The fracture (top of the figure) is rough, characteristic of a ductile fracture.
196
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - As polished micrographyDf - Fracture
The micrography of the pin at the fracture surface shows a strong plastic deformation as expected during shearing.
69
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - FeCl3+HCl+H2O Etched MicroDf - Plastic Deformation

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Dendritic branching structure of the aluminum matrix, with fine interdendritic features visible against a darker surrounding phase.
2
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Keller Etched Micrography by OMDf - Crack
ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Micrographic detail of the secondary cracks opened to the external side of the pipe. The cracks are associated to large plastic deformation.
30
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrographic detail of the ductile secondary cracks in the pipe body, close to the fracture. The strong plastic deformation is associated to the compression stresses generated by the buckling.
27
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Plastic Deformation
Micrography of a longitudinal section of the pipe at the fracture position, in the thinner thickness. The diagonal line in the middle of the figure is the fracture surface and it is possible to identify that it was sheared with strong plastic deformation. The segregation bands (longitudinal lines) are deformed in the direction of the failure shearing, in a depth that is several milimeters deep in the pipe, from the fracture surface.
17
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Fracture
Micrographic detail of sheared pipe, showing strong plastic deformation at the fracture. All the structure is deformed in the direction of the failure shearing.
17
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Plastic Deformation
ML00146 — Plastic Deformation of a SDSS Riser PinM - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Micrographic detail of the damage surface layer, detached and broken. The substrate is not affected and the rupture of the layer is typically by overloading.
117
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
ML00120 — Ductile Rupture of a Carbon Steel Eye BoltM - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Micrography of a longitudinal section of the bolt at the thread fillet adjacent to the fracture, presenting a ductile cracking from the bottom of the fillet, propagating with a strong plastic deformation. The deformation lines of the cold formed process (thread cold rolling) are also deformed by the cracking propagation.
141
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrographic detail of a longitudinal section of the bolt at the bottom of the thread fillet adjacent to the fracture, presenting a ductile cracking propagating with a plastic deformation. The deformation lines of the cold formed process are also deformed by the cracking propagation and there are some other small secondary cracks at 90° from the principal cracking.
133
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ductile Crack