Damage

4 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Standard: 898-1 Capture method: Optical Microscope clear all

Damage — sub-branches

Crack 2Cracking 3Ductile Crack 2Fracture 3Intergranular Cracking 3Secondary Cracks 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section, at the fillet that was tightened (to the end of the bolt) adjacent to the fracture. The cracking is typical of localized overloading, probably because it was only partially tightened in the tapped hole.
104
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Crack
Micrography of the longitudinal section of the bolt, at the fracture (top of the figure), starting from the bottom of the thread (to the left side of the figure). The presence of the coating at the bolt surface shows that the fracture occurred without corrosion. The rusted aspect of the fracture is associated to corrosion products after the rupture has occurred, also suggesting that the bolts were fractured and remained in service for some time after the failure occurred.
65
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Fracture
Micrography as polished of the longitudinal section of the bolt at the fracture position. The fracture (top of the figure) is rough, characteristic of a ductile fracture.
196
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - As polished micrographyDf - Fracture
Multiple intergranular cracks transverse to the bolt axis. Hydrogen assisted cracking due to cathodic protection of a high strenght steel. Micrography in the "as polished" condition.
472
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Intergranular Cracking

More from these cases

ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Micrographic detail of the cracking adjacent to the fracture. It is a secondary cracking that was created by overloading and was propagating by fatigue.
90
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Crack
ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrography, after NItal etching, of the longitudinal section of the bolt, at the fracture (top of the figure), starting from the bottom of the thread (to the left side of the figure). The presence of the coating at the bolt surface shows that the fracture occurred without corrosion.
56
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography of the longitudinal section of the bolt, in the center of the thickness, showing at the fracture surface (top of the figure), secondary cracks that are perpendicular to the fracture, associated to segregation bands.
55
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of the longitudinal section of the bolt, in the center of the thickness, showing the secondary cracks associated to segregation bands.
63
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
ML00120 — Ductile Rupture of a Carbon Steel Eye BoltM - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Micrography of a longitudinal section of the bolt at the thread fillet adjacent to the fracture, presenting a ductile cracking from the bottom of the fillet, propagating with a strong plastic deformation. The deformation lines of the cold formed process (thread cold rolling) are also deformed by the cracking propagation.
141
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ductile Crack
Micrographic detail of a longitudinal section of the bolt at the bottom of the thread fillet adjacent to the fracture, presenting a ductile cracking propagating with a plastic deformation. The deformation lines of the cold formed process are also deformed by the cracking propagation and there are some other small secondary cracks at 90° from the principal cracking.
133
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ductile Crack
ML00073 — Hydrogen Cracking of a LAS Subsea FastenerM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Micrography of a longitudinal section of the fastener, at the threat fillet, showing a transverse cracking.
68
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of the secondary crack, in the fillet adjacent to the nut position, where it was opened to the surface.
65
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrographic detail of the secondary crack, in the fillet adjacent to the nut position, where it was opened to the surface.
46
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Thin intergranular cracks in the center of the bolt thickness. Not continuous and not opened to the surface.
46
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of the intergranular morphology of the internal hydrogen cracks.
44
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking