Damage

4 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Tubular Forging Condition: Damage Capture method: Optical Microscope clear all

Damage — sub-branches

Crack 1Cracks Transverse to the Surface 1Fatigue Crack 1Layer Detachment 2Localized Corrosion 2Multiple cracks 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section, at the damage surface of the pin, where the thermal spray layer was partially detached and broken. The through layer breaking is ductile, typical of an overloading condition caused by the localized bending of the pin.
109
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
Micrographic detail of the damaged region close to the external surface, presenting a shallow localized dissolution/corrosion.
48
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Localized Corrosion
Micrography, as polished, of the transverse section of the forged pin, showing a crack in the thermal spray layer, thickness about 0.8mm. The spray and fuse process was conducted in a low alloy steel, type AISI 4130, but the quenching and tempering heat treatment was not applied later, and the pin body presented low strenght, evidencing plastic deformation after hydrostatic testing, that cause the layer cracking.
22
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - As polished micrographyDf - Cracks Transverse to the Surface
Micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing multiple cracks, typical of a corrosion fatigue mechanism.
861
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Multiple cracks

More from these cases

ML00146 — Plastic Deformation of a SDSS Riser PinM - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Micrographic detail of the damage surface layer, detached and broken. The substrate is not affected and the rupture of the layer is typically by overloading.
117
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - NaOH Electrolytic Etched MicroDf - Layer Detachment
ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Micrography of the damaged region close to the internal surface, presenting a deep pitting corrosion morphology.
40
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Localized Corrosion
ML00110 — Non Conformance in Spray and Fuse PinM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Micrographic detail of the crack in the thermal spray layer. The spray and fuse layer presented a typically melted structure with entrapped pores and globular oxides.
29
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - As polished micrographyDf - Crack
ML00082 — Corrosion Fatigue of a Drilling ToolM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
As polished micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing corrosion fatigue cracks. These are multiple cracks, paralel to the main fracture, slightly branched and fully filled with oxides.
51
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Multiple cracks
As polished micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing corrosion fatigue cracks. These are multiple cracks, paralel to the main fracture, slightly branched and fully filled with oxides.
43
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Multiple cracks
Micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing multiple cracks, typical of a corrosion fatigue mechanism.
47
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Multiple cracks
Micrography of a longitudinal section of the tubular tool, at the external surface close to the fracture position (it is to the top of the figure), showing multiple cracks, slightly branched, fully filled with corrosion products, typical of a corrosion fatigue mechanism. It propagates in a straight front, not affected by banded structures,
53
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Fatigue Crack