1 case · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Waste Heat Recovery Unit clear all

Damage — sub-branches

Crack 1Intergranular Corrosion 4Intergranular Cracking 3

Results

SortNewestOldestTitle A-ZTitle Z-A
The micrography of the transverse section of the plate, as polished, close to the surface. The material presents intergranular corrosion and some grains were lost.
1184
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OMDf - Intergranular Corrosion

More from these cases

ML00015 — Intergranular Corrosion of 304SS PlateM - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Micrographic aspect of a longitudinal section of the plate, close to the surface, in a region where it was detected intergranular corrosion up to 0,5 mm depth. As polished.
188
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OMDf - Intergranular Corrosion
Micrographic detail of intergranular corrosion, up to 0,5 mm depth. As polished.
171
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OMDf - Intergranular Corrosion
Micrographic aspect of a longitudinal section of the plate, close to the surface, in a region with intergranular corrosion. Several loose grains were removed, indicating that the structure was embrittled by the intergranular corrosion.
171
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion
Micrography of a section transverse to the repair weld showing that the macroscopic crack, detected at the surface of the plate, occurred exactly at the margin of the weld bead. It is possible to see that the bead was deposited over a region that was already corroded (intergranular corrosion) and the macroscopic crack is the opening of several corroded grains.
158
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Cracking
Detail of the fusion line region of the repair weld. It is possible to see that the cracks are filled with oxides indicating that the material was already corroded when the bead was deposited.
128
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Cracking

+2 more from this case →