Crack

2 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Hydrogen clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Hydrides in Titanium Weld
2
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Aspect by NDTDf - Crack
Low magnification micrography of another thread fillet, presenting secondary cracks from the bottom of the thread, not yet opened.
45
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Crack

More from these cases

ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
As polished micrographical detail of the cracks at the bottom of the thread fillet. There are several small cracks some of them associated to longitudinal inclusions. There are some regions presenting small "pores".
40
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Crack
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
38
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Crack
Micrography of the bottom of the thread fillet, presenting secondary cracks of intergranular morphology, not yet opened.
35
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Crack