Coarse Structure

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The coarse structure in the center of the shaft thickness is evidenced by free ferrite islands at the previous austenite grains. The presence of a pearlitic structure evidences the slow cool of the material.
85
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrographic detail of the weld metal with islands of a coarse ferritic structure, degradated (recristalized) from an acicular morphology during to the long heat treatment cycle in high temperature. The post welding heat treatment (PWHT) was conducted during 12 hours at 640°C.
700
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Coarse Structure

More from these cases

ML00152 — Low Alloy Steel Pump ShaftM - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
The longitudinal section of the shaft, at the surface, presenting only a small refining in the previous austenite grain boundaries than in the center, indicating that the material was slowed colled from forming and not heat treated.
67
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure