Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic pearlitic matrix clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a crankshaft longitudinal section at the shaft edge, in the as polished condition, presenting nodular graphite, well distruibuted.
139
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - At the Surface
The graphite nodules remain at the surface and the matrix was consumed during high temperature exposition.
103
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - At the Surface

More from these cases

ML00154 — High Strength Cast Iron CrankshaftM - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Micrography of the crankshaft at the surface, in the radio that is not heat treated. The microstructure is nodules of graphite in a ferritic and pearlitic matrix, predominantly pearlitic.
96
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the shaft at the surface, in a heat treated position. Graphite in nodules. Dark blue martensitic microstructure around the nodules and white islands of martensitic with retained austenite microstructure (not clearly identified at this low magnification).
68
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - At the Surface