Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Energy clear all

Used — sub-branches

Removed From Service 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Image of the surface of the blade, after preparation and Kalling etch, revealing the welded joint between the original casting and the insert casting adopted in the remanufacture. See the schematic drawing in the next figure
341
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Surface AspectDf - Welded Joint
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
419
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure

More from these cases

ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Schematic drawing presenting the surface of the blade
40
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Identification drawingDf - Welded Joint
Original casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
50
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Micrographic detail of the original casting blade structure. The tempered martensite is more clearly revealed by the scanning electron microscopy. The average hardness level measured in this side is 270 HV.
70
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Higher magnification of the martensitic structure of the original casting blade structure, hardness level of 270HV10.
26
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Inserted casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side

+19 more from this case →

ML00058 — High-Pressure Piston Seal in Casting Al AlloyM - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Macrography of a transverse section of the ring piston seal, shwing a thread in the internal diameter.
54
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched MacroDf - Transverse Section
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
45
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
34
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
32
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure