Shooting Effect

2 cases · 34 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: UNS Capture method: Optical Microscope clear all

Shooting Effect — sub-branches

Non-Pierced 1Pierced 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the plate in a section, in the middle of the thickness. The aligned pitting is associated to the chemical etch of inclusions and second phases. The structure is granular but the grain boundaries do not appear at that magnification, originally 50x.
50
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Aligned particles
Micrography of the plate in the middle of the thickness, showing the aligned structure tyical of a rolling process. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta

More from these cases

ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Micrography of the plate in a section, in the middle of the thickness, in a position where the plate was not affected by the shot. The microstructure is granular although the grain boundaries are not resolvable at this magnification. The black spots are localized corrosion in aligned particles.
49
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Aligned particles
Micrographic detail of the plate in the middle of the thickness. At this magnification it is possible to see the grain boundaries and the black spots are localized etching in aligned particles.
43
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Granular structure
Micrographic detail of the plate in the middle of the thickness. At this magnification it is possible to see the grain boundaries and the black spots are localized etching in aligned particles.
37
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Granular structure
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The perforated hole expulsed the material to the top and bottom directions. There are evidences of plastic deformation of the plate microstructure and the hardness level close to the hole increased from 123 HV to 131 HV (1kg)
17
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Strain Hardened
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The perforated hole expulsed the material to the top and bottom directions and the microstructure shows plastic deformation.
16
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Plastic Deformation

+10 more from this case →

ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography showing the alpha plus beta microstructure in the middle of the thickness. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
32
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the alpha (light grains as a matrix) plus beta (dark phase) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta phase (dark) in the alpha grains (light) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
24
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta (dark phase) in alpha microstructure. Etched with HF+ HNO3+H2O solution.
26
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrography by SEM of the plate in the middle of the thickness, showing the alpha microstructure (dark grains) and the beta phase (light). Etched with HF+HNO3+H2O.
35
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta

+12 more from this case →