Removed From Service

2 cases · 25 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Dendritic clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the wheel. See the schematic drawing in the next figure
467
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
419
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure

More from these cases

ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Schematic drawing presenting the position in the rim where the repair by welding was conducted. The region was machined after the welding.
77
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Identification drawingDf - Weld Repair
Profile of the rim of the wheel, total width 215 mm. See the schematic drawing in the next figure.
64
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Transverse Section AspectDf - Transverse Section
Schematic drawing indicating the location of the repair by welding
60
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Identification drawingDf - Transverse Section
Detail of the welded region in the rim of the light alloy wheel.
126
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect Before AnalysisDf - At the Surface
Aspect of the welded region after dye check showing several indications, later identified as hot cracks associated to the repair welding.
114
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect by NDTDf - Cracks

+14 more from this case →

ML00058 — High-Pressure Piston Seal in Casting Al AlloyM - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Macrography of a transverse section of the ring piston seal, shwing a thread in the internal diameter.
54
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched MacroDf - Transverse Section
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
45
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
34
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
32
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure