High Temperature

6 cases · 50 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: A Capture method: Optical Microscope clear all

High Temperature — sub-branches

Carburization 1Creep 3Microstructural Evolution 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the longitudinal section of the tube, close to the external surface. The carburizing layer consists of a bainitic structure, with intergranular and intragranular carbide precipitation.
1184
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Carburized Layer
Micrography of the new tube close to a region of a casting defect (shrinkage), presenting only austenitic structure with a network of primary precipitates.
351
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Glyceregia Etched Micrography by OMDf - Austenitic with Primary Carbides
Through wall cracking in the longitudinal seam weld of the fitting. Several cracks, longitudinal to the weld, were created by the connection of voids in the weld metal, associated to a strong microstructural evolution.
191
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Cracks
Micrography of the transverse section of the NEW TUBE, in the center of the thickness, showing the austenitic structure with primary carbides network.
410
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Austenitic with Primary Carbides
Micrography of a longitudinal section of the bolt at the fracture surface. The material showed several creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
529
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Oxide Layer
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
632
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides

More from these cases

ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrography of the longitudinal section of the tube, close to the internal surface. A thick scale is evident, but no microstructural changes compared to the center of the tube.
183
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
156
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
137
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
142
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of the longitudinal section of the tube, close to the external surface, presenting a thick deposit.
109
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - As polished micrographyDf - Close to the External Surface

+7 more from this case →

ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Micrography close to the external surface of a new tube, sound.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
Micrography close to the internal surface of a new tube, presenting casting defects.
47
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography of the tube removed from service after 6 month, close to a region of a casting defect (shrinkage), presenting austenitic structure with a network of primary precipitates (initial stage of coarsening) and intragranular secondary precipitation.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Glyceregia Etched Micrography by OMDf - Intragranular Secondary Precipitation
Micrography close to the internal surface of the tube removed from service after 6 month, presenting high temperature oxidation and shrinkage voids (casting defects).
31
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography close to the external surface of the tube removed from service, damaged by high temperature oxidation.
25
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Micrography of a longitudinal section of the fitting, at the base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
44
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrographic detail of the fitting base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrography of a transverse section of the seam weld, close to the internal surface, presenting several cracks perpendicular to the thickness.
37
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrographic detail of the seam weld close to the internal surface, presenting the needles that are the result of microsctructural evolution and cracks filled with oxides.
36
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrography of a transverse section of the seam weld, in the middle of the thickness, presenting several parallel cracks.
27
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - In the Center of the Thickness

+7 more from this case →

ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Micrography of the transverse section of the NEW TUBE, close to the external surface, showing the austenitic structure with primary carbides network.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects close to the external surface.
49
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Close to the External Surface
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects in the center of the thickness.
47
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Transverse Section
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE, in the center of the thickness, showing the austenitic structure with primary carbides network and secondary precipitation.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Intragranular Secondary Precipitation
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE,close to the external surface, showing the austenitic structure with coalesced carbides and secondary precipitation.
39
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface

+2 more from this case →

ML00004 — Creep in High Temperature BoltsM - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
121
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Interconnected Cracks
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
101
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Voids
Micrography of a longitudinal section of a CrMov steel bolt that broke in service by a creep mechanism in a gas turbine. Tempered structure. Interconnected cracks paralled to the fracture surface.
95
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Crack
Micrographic detail of a longitudinal section of the bolt far from the fracture, presenting a tempered structure.
82
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Tempered Structure
Micrographic detail of a longitudinal section of the bolt close to the fracture, presenting an overtempered structure.
76
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Overtempered Structure
ML00003 — Cast iron Engine Valve SeatsM - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
206
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
182
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
137
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure