Fabrication Defect

3 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Optical Microscope Detail focus: Longitudinal Section clear all

Fabrication Defect — sub-branches

Casting Defect 1Coating Defect 1Heat Treatment Defect 4Not according to spec 4Welding Defect 9

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
61
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
Shaft microstructure in the longitudinal section, showing aligned segregations typical of the material forming.
31
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
13Cr SS longitudinal section micrography, at the collapsed region, showing a ferritic matrix structure (overtempered) with the previous austenite grain boundaries decorated by phases (carbides and probably martensite islands), indicating that the material was exposed to a high tempering temperature that created a partial austenitizing condition. It explains the material low toughness and lower strenght (than required).
437
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00123 — Non Qualified Superduplex for SubseaM - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. The average austenite spacing is 80 microns, a lot larger than the maximum allowed in the specification, of 30 microns. No detrimental phases were identified at the ferrite/austenite interfaces, but the ferrite phase presented a rough aspect. Higher magnification analysis would be required to identify precipitation.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
ML00039 — Collapse in Tubular 13CrM - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
13Cr SS in the longitudinal section, at the collapsed region. Non uniform structure (ferritic matrix and decorated prior austenite grain boundaries) that evidences an usuitable heat treatment during fabrication, and explains the material low strenght.
54
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section