Damage

2 cases · 46 images for “ductile behavior”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Damage — sub-branches

Ductile Behavior 2

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 1) that broke during a car accident on a road.
1644
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Lateral image of a collapsed API 5D grade S135 drill pipe, presenting the fractured region (bottom of the figure) at the pipe body. Although the pipe steel is of a high strenght, the fracture characteristic is ductile, evidencing strong plastic deformation.
545
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Front wheel 17 x 7J of a passenger vehicle (identified as WHEEL 2) that cracked exactly in the same location that the other front wheel broke.
91
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Aspect of the two wheels before disassembling the tires.
75
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - General View
Detail of the fracture in the WHEEL 1, changing direction of propagation.
71
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Fracture
Detail of the crack in the WHEEL 2, changing direction of propagation exactly like the other whel.
66
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Cracking
Low magnification view of the WHEEL 1 fracture surface. The thickness of the wheel in this position (flat and paralell to the wheel face) is about 2.5 mm. The aspect of the fracture is similar all through the fracture perimeter, including the region where the fracture propagation changes the direction.
66
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Fractography by SEMDf - General View

+24 more from this case →

ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Tempered martensite of the pipe body of this API 5D grade S135 drill pipe. The material presents, at this low magnification micrographic aspect, a slightly banded structure, usual for this type of drill pipe.
58
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body. Uniform structure.
44
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensite in the longitudinal section of the pipe body.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Martensite
Macroscopic view of the fracture in the pipe body. In the bottom of the figure, the fracture of the pipe shows a thicker thickness, revealing that this is the pipe region that was first damaged by bending (buckling). In the top of the figure, the fracture shows a (ductile) shearing mechanism and the thickness is thinner, as will be better observed in the macrography.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Fracture
Macrography of a longitudinal section of the pipe at the fracture position, as ground, showing in the rigth side the thicker thickness and several secondary cracks opened to the external side of the pipe (created during bending), and in the left side the shearing mechanism and the thinner thickness.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Longitudinal Section AspectDf - Plastic Deformation

+10 more from this case →