Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic matrix Capture method: Optical Microscope Detail focus: Damage clear all

Damage — sub-branches

Brittle Behavior 1Corrosion 1High Temperature 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The micrography of the stem at the fracture region shows a flat fracture with transgranular clevage at the ferritic structure.
137
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
The micrography of a longitudinal section of the pipe, close to the internal surface, shows a general corrosion mechanism (with slow wall thickness loss), although the graphite/matrix interface is corroded preferentially.
569
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion

More from these cases

ML00040 — Brittle Fracture of a Valve StemM - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Micrography presenting a detail of the fracture surface opening to the graphite nodules.
139
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
ML00034 — 45 Years Old Acquaduct Grey Cast IronM - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Micrography of the longitudinal section of the pipe, at the external surface. Oxides and general corrosion.
122
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion