Damage

3 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Segregation Bands Capture method: Longitudinal Section Aspect clear all

Damage — sub-branches

Brittle Behavior 2Ductile Behavior 1Fabrication Defect 3Fatigue 1Hydrogen 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Longitudinal section of the cylindrical body showing two pieces with the cracks, close to the position of the actuator hole. The valve body thickness is 40 mm at the location where the cracks appeared.
53
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Longitudinal Section AspectDf - Crack
Macrography of a longitudinal section of the pipe at the fracture position, as ground, showing in the rigth side the thicker thickness and several secondary cracks opened to the external side of the pipe (created during bending), and in the left side the shearing mechanism and the thinner thickness.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Longitudinal Section AspectDf - Plastic Deformation
The longitudinal macrosection shows the fracture appearance, irregular, and a lot of secondary cracks transverse to the bolt axis, and longitudinal.
126
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section

More from these cases

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Valve Body Crack Growth from Weld Defects
2
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Longitudinal Section AspectDf - Crack
ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Several secondary cracks in the broken bolt, responsible for the irregular shape of the fracture, that presentes brittle cracks in the transverse and longitudinal directions.
109
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section