Damage

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Kalling Etched Micrography by OM Detail focus: Plastic Deformation clear all

Damage — sub-branches

Brittle Behavior 12Corrosion 39Ductile Behavior 5Fabrication Defect 20Fatigue 12High Temperature 9Hydrogen 17Lack of Sealing 1Repair Defect 1Shooting Effect 4Wear 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the nut in the longitudinal section, plastic deformation at the thread surface due to high local stresses, probably during assembling.
24
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Plastic Deformation
Micrographic detail of the threaded body to bolt heat transition region, showing a variation in the grain size (of the previous austenite) and evidences of a deformed structure .
43
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Plastic Deformation

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Micrographic detail of the nut in the longitudinal section, presenting cracks associated to the plastic deformation at the thread surface. These cracks were formed due to high local contact stresses.
19
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Plastic Deformation