Damage

5 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite Capture method: Fracture Surface Aspect clear all

Damage — sub-branches

Brittle Behavior 4Corrosion 5Ductile Behavior 1Fabrication Defect 5Fatigue 2High Temperature 1Hydrogen 7Shooting Effect 1

Results

SortNewestOldestTitle A-ZTitle Z-A
View of the fracture. The internal green coating was removed only close to the fracture.
29
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Fracture Surface AspectDf - Fracture
Fracture appearance of one side of the broken part showing chevron marks coming from the thinner part of the fracture. The socket thickness is only 13 mm at this point.
77
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
The fracture is flat, in the region of the lower resistant section, presenting no macroscopic evidences of plastic deformation. The starting point of the fracture is indicated by the chevron marks.
62
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks
Detail of the flat fracture surface of the pin, after disassembling from the TJ box. ID in the top and OD in the bottom of the figure. Radial marks are clear in the fracture surface.
57
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Aspect of the all weld metal broken tensile test conducted in the sample removed from structure close to the region where the cracking was detected, indicating that the material entrapped hydrogen for several days, since the test was conducted more than 2 weeks later than the cracking was detected.
61
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Fracture Surface AspectDf - Fish Eye

More from these cases

ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Fracture appearance of the other side of the broken part, also evidencing chevron marks coming from the thinner part of the fracture.
63
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Detailed macroscopic aspect of the chevron marks in the fracture, starting at the internal surface of the socket, in a region in contact with the bolt that was being torked. The thickness socket is 13 mm at this point.
54
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Chevron Marks
Detailed macroscopic aspect of the chevron marks in the other side of the fracture, starting at the internal surface of the socket, in a region in contact with the bolt that was being torked. The thickness socket is 13mm at this point.
51
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Chevron Marks
ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Macroscopically brittle fracture of the barrel nut, starting at the edge of the thread, as shown by the chevron marks.
29
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks