Damage

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 479 Capture method: Aspect Before Analysis clear all

Damage — sub-branches

Corrosion 1Ductile Behavior 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the male part of the coupling, a pin, presenting the thermal spray layer detachment (right side of the figure). The pin was manufactured in a superduplex stainless steel tubular forging; the external surface was partially coated by thermal spray and machined. The sealing is only elastomeric but a coating is required to avoid galling between the two materials of the coupling.
1154
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - Aspect Before AnalysisDf - Layer Detachment
Aspect of the Nitronic 60 cylinder, OD 36.4mm, presenting pits at the external surface.
219
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface

More from these cases

ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Aspect of the 17-4 PH rod, OD 10.6 mm, presenting deep pits at the external surface.
125
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface