Damage

3 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Bar Capture method: Aspect Before Analysis clear all

Damage — sub-branches

Brittle Behavior 1Ductile Behavior 1Fabrication Defect 1Fatigue 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the broken shear pin that was manufactured in a martensitic stainless steel forged bar, machined with the external diameter of 50mm, the internal diameter of 20mm and the shearing diameter of 25mm (shearing thickness 2.5mm). The fracture, in the right side of the figure, is not fully flat as should be expected for a shearing mechanism.
55
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
498
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
The fracture surface is flat and smashed due to the shearing action.
87
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Aspect Before AnalysisDf - Fracture

More from these cases

ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
xx
117
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
120
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture