Damage

3 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Forging Microstructure: Tempered Martensite Capture method: Aspect Before Analysis clear all

Damage — sub-branches

Corrosion 1Fabrication Defect 2

Results

SortNewestOldestTitle A-ZTitle Z-A
The drilling connector, 21" diameter, presented a crack at the margin of the weld in the forging side (left side of the weld in the figure).
745
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the crack in the valve ring surface. A leakage was detected during testing after 6 months out of service and the inspection identified several transverse cracks in the forged ring. The valve was installed for one year, but it was not drained during the time it was out of service. The cracks were located in regions that were rusted and presenting a biological fouling.
50
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - At the Surface
The connector was welded to the pipe from both (internal and external) sides, a PWHT was applied and the part was machined. The UT indication was detected during final inspection.
78
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00178 — Cold cracks in Cr-Mo Welded ForgingM - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Circumferential weld aspect. Two passes in the cap. This forging to pipe welded joint, 22 mm thick, was welded by an automatic process in a narrow gap. The pipe is to the top of the image and the forging is to the bottom of the image.
165
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - External Surface
ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Macroscopic aspect of the crack after cleaning the ring surface. Transverse cracks were identified associated to pitting corrosion.
44
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Localized Corrosion