Damage

3 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic Capture method: Aspect Before Analysis Detail focus: Sampling and Analysis clear all

Damage — sub-branches

Brittle Behavior 1Corrosion 1Fabrication Defect 3Fatigue 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Gas piping. Aspect of a branching line 2" ND with a flange, lateral to a main pipe ND 8", welded using a weldolet. The cracking is at the margin of the weld.
115
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Aspect of the external side of the connector, with a longitudinally crack of a brittle aspect. It is a 5/8" connector (15.8 mm).
134
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the fillet weld between the superior plate (Low carbon 8 mm thick) and the inferior plate (C-Mn 12 mm thick), in an overlap geometry. In this region the welded joint was sound.
90
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Welded Joint

More from these cases

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. In the lower part of the branch there are no cracks.
61
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the brach line viewed from the internal side of the main pipe, after cuting. It is possible to see that the pipe was perforated by a thermal cutting (looking the finishing aspect of the edge of the hole). The weldolet was welded only from the external side of the pipe.
62
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface