Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Aspect Before Analysis Detail focus: Localized Corrosion clear all

Damage — sub-branches

Brittle Behavior 12Corrosion 39Ductile Behavior 5Fabrication Defect 20Fatigue 12High Temperature 9Hydrogen 17Lack of Sealing 1Repair Defect 1Shooting Effect 4Wear 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the external side of the nominal diameter 6 3/4" drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained for a period a little longer than 1 month. This tool is a high strength steel, cold worked.
125
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Localized Corrosion
Macroscopic aspect of the crack after cleaning the ring surface. Transverse cracks were identified associated to pitting corrosion.
44
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Localized Corrosion
Aspect of a crevice corrosion of the flange, under the bolt head, showing evidences that the cathodic protection system was not connected to the stainless steel instrument.
1434
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Localized Corrosion
Deep localized corrosion spots, rusted. There are indications that the roughness of the surface influences the localized corrosion location.
61
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Localized Corrosion

More from these cases

ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
The case where the electronic device was installed suffered a localized corrosion that allowed the seawater to wet the internal side, destroying it. The position where the leakage occurred originally presented a hole that was sealed with a plug and the corrosion occurred in a crevice condition.
166
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Localized Corrosion